5/8/10mm B1 Fireproof Acrylic Panel Hospital Partition Sheet-Anhui Jinbaijie New Material Technology Co., Ltd

Product Details

Key Attributes

Material	acrylic acid	Thickness	1-50mm(0.04−1.97in)
Processing Services	Mold making ,cutting	Country of Origin	Anhui,China
Model	acrylic acid	Brand	Jinbaijie
Size	1220 * 2440mm，2050 * 3050mm or customized	Product Name	Flame-retardant acrylic sheets
Color	Customized	Raw Materials	100% Virgin Mitsubishi MMA
Light Transmittance	93%	Density	1.2g/cm3
Thickness	1-50mm	Packaging	Both sides coated with PE film or brown kraft paper
MOQ	500kgs	Delivery	7-25days
Application	Advertising,sign,furniture,crafts,bathtub,windows,door

Sales Unit

Single Item

Single Package Dimensions

34 x 30x 6 cm

Single Product Gross Weight

1.000 kg

Supplier's product description

Features:

1. UL94 V-0 high fire safety rating

2. Non-dripping char formation and heat-resistant structural integrity

3. Versatile manufacturing capabilities and environmental durability

Dimensions: 1220mm x 2440mm; 2000mm x 3000mm; 1000mm x 2000mm (customization available)

Thickness: 1–50mm

Packaging: Covered with double-sided PE film or kraft paper; packed on wooden pallets.

Product Name:	Flame-retardant Acrylic Sheet
Color:	Customized
Material:	100% Virgin Mitsubishi MMA
Thickness:	1–50 mm
Dimensions:	1220×1830 mm / 1220×2440 mm / 2050×3050 mm or customized
Density:	1.2 g/cm³
Surface:	High hardness and flatness
Packaging:	PE film or kraft paper
Logo:	Customization available
Applications:	Advertising, construction, decoration, industry

Property	Value	Standard
Density	1.19 g/cm³	ISO 1183-1:2012 Method A
Rockwell Hardness	112 L	ISO 2039-2:1999
Tensile Modulus	3150 MPa	ISO 527:2012
Tensile Strength	80.0 MPa	EN ISO 527:2012
Tensile Strain at Break	3.2%	ISO 527-1:2012
Water Absorption	0.20%	ISO 62:2008 Method 1
Total Light Transmittance	93.4%	ISO 13468-1:1996
Vicat Softening Temperature	105°C	ISO 306:2013 Method B50
Photo-aging Test - UV Exposure	Grey Scale: 5	ISO 4892-3:2016 Cycle 1
Mean Coefficient of Linear Thermal Expansion	72 × 10⁻⁶ K⁻¹	ISO 11359-1:2014
Compressive Stress at Yield	129 MPa	ISO 604:2003
Flexural Strength	120 MPa	ISO 178:2013
Compressive Yield Strength	111 MPa	ASTM D695-15
Compressive Modulus	3450 MPa	ASTM D695-15
Shear Strength	59.7 MPa	ASTM D732-17
Deflection Temperature Under Load	100.2°C	ASTM D648-18 Method B
Modulus of Elasticity	2810 MPa	ASTM D695-15