Custom Cut 2.5mm Marble Acrylic Hotel Wall Panels-Anhui Jinbaijie New Material Technology Co., Ltd

Product Details

Key Attributes

Material	Acrylic acid	Thickness	1-30mm(0.04−1.18in)
Material Properties	Flame retardant, UV resistant, anti-aging, oil resistant	Processing Services	Mold making ,cutting
Country of Origin	Anhui,China	Model	JBJ-2101
Brand	Jinbaijie	Dimensions	12202440mm,20503050mm or customized
Product name	Marble Acrylic sheet	Color	Customized
Raw Material	100% Virgin Mitsubishi MMA	Light Transmittance	93%
Density	1.2g/cm3	Thickness	1-30mm
Packaging	Both Sides with PE Film or Brown Craft Paper	MOQ	500kgs
Delivery	7-25 Days	Application	Arts&Crafts,Decorations,Signage &Displays,Architectural

Sales Unit

Single Item

Single Package Dimensions

34 x 24 x 6 cm

Single Product Gross Weight

1.000 kg

Supplier's product description

Features:

1. Customized patterns that showcase the beauty of natural marble.

2. Enhanced physical properties compared to natural stone.

3. Manufacturing versatility and environmental durability.

Dimensions: 1220mm x 2440mm; 2000mm x 3000mm; 1000mm x 2000mm (customization available)

Thickness: 1–30mm

Packaging: Double-sided PE film or kraft paper masking; packed on wooden pallets

Product Name:	Marble-effect Acrylic Sheet
Color:	Customized
Material:	100% Virgin Mitsubishi MMA
Thickness:	1–30 mm
Dimensions:	1220×1830 mm / 1220×2440 mm / 2050×3050 mm or customized
Density:	1.2 g/cm³
Surface:	High hardness and high flatness
Packaging:	PE film or kraft paper
Logo:	Customizable
Applications:	Architecture, decoration, arts and crafts

Property	Value	Standard
Density	1.19 g/cm³	ISO 1183-1:2012 Method A
Rockwell Hardness	112 L	ISO 2039-2:1999
Tensile Modulus	3150 MPa	ISO 527:2012
Tensile Strength	80.0 MPa	EN ISO 527:2012
Tensile Strain at Break	3.2%	ISO 527-1:2012
Water Absorption	0.20%	ISO 62:2008 Method 1
Total Light Transmittance	93.4%	ISO 13468-1:1996
Vicat Softening Temperature	105°C	ISO 306:2013 Method B50
Light Aging Test - UV Exposure	Grey Scale: 5	ISO 4892-3:2016 Cycle 1
Mean Coefficient of Linear Thermal Expansion	72 × 10⁻⁶ K⁻¹	ISO 11359-1:2014
Compressive Stress at Yield	129 MPa	EN ISO 604:2003
Flexural Strength	120 MPa	ISO 178:2013
Compressive Yield Strength	111 MPa	ASTM D695-15
Compressive Modulus	3450 MPa	ASTM D695-15
Shear Strength	59.7 MPa	ASTM D732-17
Heat Deflection Temperature	100.2°C	ASTM D648-18 Method B
Modulus of Elasticity	2810 MPa	ASTM D695-15